`n_{Fe_2(SO_4)_3}=(62)/(400)=0,155(mol)`

Quy đổi hh thành `Fe:0,31(mol); O:x(mol)`

`->0,31.56+16x=21,68`

`->x=0,27`

Bảo toàn `e:` `n_{SO_2}=(0,31.3-0,27.2)/(2)=0,195(mol)`

`V=0,195.22,4=4,368(l)`

Quy hh thành `Fe[x(mol)]; Fe_3O_4[y(mol)]`

`=> 56x + 232y = 21,68(1)`

`2Fe + 6H_2SO_{4đ,nóng} -> Fe_2(SO_4)_3 + 3SO_2 + 6H_2O`

`2Fe_3O_4 + 10H_2SO_{4đ,nóng} -> 3Fe_2(SO_4)_3 + SO_2 + 10H_2O`

Theo PTHH:

`n_{Fe_2(SO_4)_3} = 1/2n_{Fe} + 3/2n_{Fe_3O_4} = 1/2x + 3/2y = {62}/{400} = 0,155(mol)(2)`

`(1), (2)`

`=> x = 0,1075; y = 0,0675`

Theo PTHH

`n_{SO_2} = 3/2n_{Fe} + 1/2n_{Fe_3O_4} = 3/2 . 0,1075 + 1/2 . 0,0675 = 0,195` mol

`=> V = V_{SO_2} = 0,195 . 22,4 = 4,368l`